810——(underwater、fast) Epoxy Curing Agent

With the development of our nation's economic construction, more and more epoxy resins are needed under humidity or water. However,epoxy binders compounded by ordinary epoxy curing agents aren't effective enough. The epoxy binder compoun-ded by 810-underwater epoxy curing agent can be solidified and bonded not only in the air but also under moisture or water. Such bond and the cohesional strength of concrete go beyond the demands of common water conservancy project, thus this curing ag-ent is applied to the defect disposal of buildings like dams, tunnels, water pipelines, pools, aqueducts, civil air defense projects and the underwater bond of other ce-ment products. In recent years,it is widely used in the field of metallurgy,smelting,mining machine manufactu-re,molding,military antisepsis and underground cable,etc. This curing agent can be used under conditions like under water, moisture, dryness,low temperature(under 0 centi-grade) and normal temperature and has good underwater cohesional strength so it can meet the demands of underwater construction projects and winter construc-tion. With low toxicity(LD>5000mg/kg), this curing agent is slightly poiso-nous or actually nonpoisonous and has the features of heat and cold resistance. The technological and economic benefit of its application are both notable.

Product standards of810-underwater epoxy curing agent:

Appearance: brown and sticky, translucent liquid

Amine value：350-410mgKOH/g

Viscosity：3-6Pa·s(25℃)

Specific gravity：1.056-1.150(20℃)

Freezing point：below -14℃

Saturated steam pressure：3.09Pa(25℃)

Toxicity：LD50>5000mg/kg

Polyamine——105 Epoxy Resin Curing Agent

With low toxicity, Polyamine-105 can be solidified under normal temperature and is easy to use. The epoxy resin made up by this product has a bright and clean appearance,no blooming,good sealing,low accessibility,a higher distortion tempe-rature and shear strength. Its electrical function (like insulation) and abra-sion performance are particularly excellent.Therefore, this product is generally used in pouring, laminating, sealing,bonding and abrasive coating,especially the sealing of electrical equipment,the sealing and pouring of water purification f-ilm,the slideway of machine tool as well as the abrasive and anticorrosive pat-ching material for mechanical and chemical equipment.

Appearance: jasmine,transparent,sticky liquid

Amine value: approx 550 viscosity500-1,000

Toxicity：LD50>3493mg/kg

Steam pressure: 5.012×10-5mmHg(25℃)

Condition of cure:ambient temperature,better curing performance under medium te-mperature(80℃/3h or 100℃/2h)

sable life: blended with 618# epoxy resin at 25℃, 30 minutes of usable life

Apart from the performance of acid,alkali and salt fastness as the ordinary epoxy resin products,its mechanical and electrical functions are as follows:

Note:

1.N is glass fibre reinforced plastic formed by handpaste (glue percentage 45%-50%).

2. Formula is a ratio of weight.

The follow is the product performance in the abrasive coating of machine tool slideway：

 

800 Epoxy Resin Curing Agent

As a kind of modified amine curing agent with low toxicity and volatility, 800 epoxy resin curing agent can be fully solidified under moisture and low temp-erature. After its solidification, the product has the features of heat and cold resistance and good flexibility.This product can be applied to chemical indu-stry,metallurgy,construction anticorrosion,mechanic mold,epoxy antisepsis coat-ing,the production of glass fiber reinforced plastic and adhesion agent,grouting and blockage of water conservancy and water electricity.

Appearance: brown, sticky liquid

Viscosity：(mpa·s)：3000-6000

Amine value:(mgKOH/g):360-420

Toxicity：LD50>3690·mg/kg·bw

 

810 Epoxy Resin Curing Agent810

Developed by our institute, 810 epoxy resin curing agent is specially used in the field of anticorrosion. With low toxicity,good acid and alkali fastness, wi-de scope of heat resistance and wet fastness, this curing agent can completely solidify epoxy resin under conditions like low temperature,humidity, ambient te-mperature with dryness and under water. With its excellent performance, the ag-ent is widely used in chemical mine,metallurgy and smelting,mechanical elec-tric power,construction,water conservancy and water electricity, various epoxy anti-sepsis coating, the making of glass fibre reinforced plastic,adhesive and seal-ing material,grouting and blockage.

Appearance: brown red,translucent,sticky liquid

Amine value: 380-450(mgKOH/g)

Viscosity: 3-6pa·s/25℃

Freezing point:below -14℃

Toxicity: LD50>5000·mg/kg(slightly poisonous or actually non-poisonous)

Condition of cure: ambient 12h-24h

Colloid compression strength>83Mpa

Colloid tensile strength>28Mpa

Underwater cohesional strength: The "8" shape test parts of cement sand mortar is 2.6Mpa; In normal condition, it is 1.5-2.6Mpa, the tensile strength of sticked glass cloth : 100-134.8Mpa

Modulus of elasticity：3136Mpa

Metal plane butt tensile strength：Mpa

Constant temperature heat test:After 360 hours at 60℃ and 95% relative humidi-ty, the agent shows no decline of tensile strength, which proves its good heat-resistance.

Circulating freeze-thaw test: Freezed in fridge at -20±2℃ and thawed at ambie-nt temperature （about 35℃）for 864 hours, the agent has no decline of tensile strength after 69 circulating tests, which indicates its good cold-resistance.

50 Modified Amine Epoxy Curing Agent

This agent,one of our new amine curing products, has a lower freezing point,a higher boiling point and good fluidity and it is easy to use.Its performance is superior to xylylene amine and ethylenediamine. An ideal epoxy resin curing age-nt with low toxicity, this product is applied to the manufacture of glass fiber reinforced plastic,the inside antisepsis coating of gaint equipment, plastic mo-ld and sealing material of electric equipment.

Main Physical Constant of A50 Modified Amine

specific gravity：1.054	diopter：1.5603
viscosity：16CP	freezing point：<-14℃

 

A60 Epoxy Resin Curing Agent

As a kind of modified amine curing agent with low toxicity, A60 curing agent has a light color, low viscosity, easy operation and medium curing speed. Meanwhile, it also has a long molecular chain, a high boiling point, low volatility and to-xicity and the toughness and electrical performance of the condensate are exce-llent.

Appearance:jasmine,transparent liquid

Viscosity：mpa·s ≥100

Amine value：mgKOH/g 430-480

Toxicity：LD50 > 3106mg/kg·bw（low toxicity）

Being an epoxy resin curing agent of ambient temperature, A60 curing agent is used to compound epoxy coating,antisepsis coating,adhesion agent and to produce glass fiber reinforced plastic, casting mold and the sealing material of elec-tronics and electrical equipment. The normal dosage is 20%-28% of epoxy resin.

Conditions of cure: 48 hours at normal temperature (60℃ is preferable),solidified for 4 hours

 

A70 Epoxy Resin Curing Agent

As a modified amine epoxy resin curing agent with low viscosity, A70 curing ag-ent has the features of low toxicity, strong toughness,shiny appearance, good sealing performance and long application period. It is applied to various kinds of pouring sealants for electronic and electrical equipments,accumulator and ca-pacitor,etc. It is the most preferable material for epoxy pouring material and can be used in the manufacture of coating and glass fibre reinforced plastic.

Appearance:jasmine to brown yellow,transparent liquid

Viscosity：(mPa·s)50-100

Amine value：(mgKOH/g) 480-550

100g E51 epoxy resin with 30-80g A70(reducing the dosage if adding other accessory ingredients)

Application period(100g):ambient temperature(25℃)，over 1h (25℃)，24-48h或60℃ 4h

Time and conditions of cure: ambient temperature (25℃)，24-48h or 60℃ 4h

T31 Modified Epoxy Curing Agent

Modified by phenol aldehyde, T31 modified curing agent has lower volatility and toxicity and takes the place of traditional ethylenediamine. It can solidify epoxy resin under the conditions of room,normal or low temp-erature, moisture,dryness and conditions of low demand of formula dosage. With excellent physical and chemic-al performance, it has performance of insulation, wat-er proof,oil resistance,acid-alkali resistance, abras-ive fastness and chemical resistance. The agent is wi-dely used not only in the production of antisepsis co-ating in the the fields of aerospace and war indust-ry,machine,vehicle and ship,petroleum and chemical,metallurgy and smelting, con-struction but also in the manufacture of glass fibre reinforced plastics and plastic mold products. Moreover, it is used in on-the-spot construction,the pro-duction of sealing agent of adhesion agent material,grouting and pouring, etc.

Appearance: brown,red,transparent liquid

Amine value：500±50(mgKOH/g)

Viscosity：1000-5000(mpa·S25℃)

Condition of cure：4h-24h